很多人都说中空玻璃充氩气是为了防止中空玻璃起雾?但是双组份打胶机厂家告诉你,其实这个说法是不正确的!那么,既然充入惰性气体不能防止起雾,那么它有什么作用呢?以氩气为例,以下几点才是它真正的作用:
Many people say that the filling of argon in hollow glass is to prevent the fogging of hollow glass? But the manufacturer of two-component glue machine tells you that this statement is incorrect. So, since filling inert gas can not prevent fogging, what role does it play? Take argon as an example, the following are its real functions:
(1)充氩气后可以减少内外压力差,保持压力平衡,减少由于压力差引起的玻璃炸裂。
(1) After filling with argon, the pressure difference between inside and outside can be reduced, the pressure balance can be maintained, and the glass burst caused by the pressure difference can be reduced.
(2)充气氩气后,可以有效改善中空玻璃的K值,减少室内侧玻璃的冷凝,改善舒适水平,即充气后的中空玻璃更不容易出现结露和上霜,但不充气不是导致起雾的直接原因。
(2) The K value of the hollow glass can be effectively improved after argon gas filling, which can reduce the condensation of the indoor side glass and improve the comfort level. That is to say, the hollow glass after gas filling is less prone to condensation and frost, but not inflatable, which is not the direct cause of fogging.
(3)由于氩气作为惰性气体自身所具有的特性可以减慢中空玻璃内的热对流,同时也可以更大幅度地提高其隔音降噪效果,即可以使中空玻璃的保温,隔音效果更好。

中空玻璃生产线
(3) As an inert gas, argon can slow down the heat convection in hollow glass, and can also greatly improve its sound insulation and noise reduction effect, that is to say, it can make the insulating effect of hollow glass better.
(4)可以增加大面积中空玻璃的强度,使其中间不会因为没有支撑而塌陷。
(4) It can increase the strength of large area hollow glass, so that it will not collapse because there is no support in the middle.
(5)增加抗风压强度。
(5) Increase the wind compressive strength.
(6)因为充入的是干燥的惰性气体,可以将中空腔体内的带有水份的空气置换出去,使腔体内环境保持更干燥,延长铝间隔条框内分子筛的使用寿命。
(6) Because it is filled with dry inert gas, the water-bearing air in the hollow chamber can be replaced, so that the inner environment of the chamber can be kept drier and the service life of the molecular sieves in the aluminium spacer frame can be prolonged.
(7)在使用低辐射LOW-E玻璃或镀膜玻璃时,由于充入气体为不活泼惰性气体,可以保护膜层降低氧化速度,延长镀膜玻璃的保用寿命。
(7) When using low-radiation LOW-E glass or coated glass, because the gas is inert, the oxidation rate of the coated glass can be reduced and the service life of the coated glass can be prolonged.
本文由双组份打胶机厂家友情奉献.更多有关的知识请点击:http://www.!我们将用先进的技术.真诚的态度.为您提供为全面的服务.更多有关的知识我们将会陆续向大家奉献.敬请期待。
This article is dedicated by the two-component glue maker. For more information, please click: http://www.! We will use advanced technology and sincere attitude to provide you with comprehensive services. More relevant knowledge will be dedicated to you one after another. Please look forward to it.

友情链接:    九五棋牌代理   TH炸金花   夺宝棋牌网站   金龙棋牌手机客户端   彩票网投app